Chlorinated Polyethylene for Magnetic Products
Chlorinated polyethylene for Magnetic Products
|
Item |
Unit |
Type |
||||
|
CPE3615G |
CM2500A |
CM2500B |
CPE230A |
CPE230B |
||
| Chlorine Content | % | 36±2 | 25±2 | 25±2 | 30±2 | 30±2 |
| Heat of Fusion | J/g | ≤5.0 | ≤10.0 | ≤2.0 | ≤2.0 | ≤2.0 |
| Shore Hardness | A | ≤60 | ≤80 | ≤80 | ≤70 | ≤67 |
| Tensile Strength | Mpa | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 |
| Elongation at Break | % | ≥800 | ≥600 | ≥600 | ≥800 | ≥800 |
| Volatile Content | % | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 |
| Mooney Viscosity | ML125℃ 1+4 | 80-90 | 76-82 | 64-70 | 80-90 | 60-70 |
| Note: Please confirmed with us when you have special requirements . | ||||||
|
Item |
Unit |
Type |
||||
|
CPE3615G |
CM2500A |
CM2500B |
CPE230A |
CPE230B |
||
| Chlorine Content | % | 36±2 | 25±2 | 25±2 | 30±2 | 30±2 |
| Heat of Fusion | J/g | ≤5.0 | ≤10.0 | ≤2.0 | ≤2.0 | ≤2.0 |
| Shore Hardness | A | ≤60 | ≤80 | ≤80 | ≤70 | ≤67 |
| Tensile Strength | Mpa | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 | ≥8.0 |
| Elongation at Break | % | ≥800 | ≥600 | ≥600 | ≥800 | ≥800 |
| Volatile Content | % | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 | ≤0.40 |
| Mooney Viscosity | ML125℃ 1+4 | 80-90 | 76-82 | 64-70 | 80-90 | 60-70 |
| Note: Please confirmed with us when you have special requirements . | ||||||